Physio-mechanical Properties of Aluminium Metal Matrix Composites Reinforced with Al2O3 and SiC
Abstract:
Particulate reinforced metal matrix composites (MMCs) are potential materials for various applications due to their advantageous of physical and mechanical properties. This paper presents a study on the performance of stir cast Al2O3 SiC reinforced metal matrix composite materials. The results indicate that the composite materials exhibit improved physical and mechanical properties, such as, low coefficient of thermal expansion, high ultimate tensile strength, high impact strength, and hardness. It has been found that with the increase of weight percentage of reinforcement particles in the aluminium metal matrix, the new material exhibits lower wear rate against abrasive wearing. Being extremely lighter than the conventional gray cast iron material, the Al-Al2O3 and Al-SiC composites could be potential green materials for applications in the automobile industry, for instance, in making car disc brake rotors.
Keywords:
Metal Matrix Composite, Strength to Weight Ratio, Wear Rate
2
11911
A Parametric Study: Frame Analysis Method for Masonry Arch Bridges
Abstract:
The predictability of masonry arch bridges and their behaviour is widely considered doubtful due to the lack of knowledge about the conditions of a given masonry arch bridge. The assessment methods for masonry arch bridges are MEXE, ARCHIE, RING and Frame Analysis Method. The material properties of the masonry and fill material are extremely difficult to determine accurately. Consequently, it is necessary to examine the effect of load dispersal angle through the fill material, the effect of variations in the stiffness of the masonry, the tensile strength of the masonry mortar continuum and the compressive strength of the masonry mortar continuum. It is also important to understand the effect of fill material on load dispersal angle to determine their influence on ratings. In this paper a series of parametric studies, to examine the sensitivity of assessment ratings to the various sets of input data required by the frame analysis method, are carried out.
Keywords:
Arch Bridge, Frame Analyses Method, Masonry
1
14729
Performance of Concrete Grout under Aggressive Chloride Environment in Sabah
Abstract:
Service life of existing reinforced concrete (RC) structures in coastal towns of Sabah has been affected very much. Concrete crack, spalling of concrete cover and reinforcement rusting of RC buildings are seen even within 5 years of construction in Sabah. Hence, in this study a new mix design of concrete grout was developed using locally available materials and investigated under two curing conditions and workability, compressive strength, Accelerated Mortar Bar Test (AMBT), water absorption, volume of permeable voids (VPV), Sorptivity and 90-days salt ponding test were conducted. The compressive strength of concrete grout at the age 90 days was found to be 44.49 N/mm2 under water curing. It was observed that the percentage of mortar bar length change was below 1% for developed concrete grout. The water absorption of the concrete grout was in between the range of 0.88 % to 3.60 % under two different curing up to the age 90 days. It was also observed that the VPV of concrete was in the range of 0 % to 9.75 and 2.44% to 13.05% under water curing and site curing respectively. It was found that the Sorptivity of the concrete grout under water curing at the age of 28 days is 0.211mm/√min and at the age 90 day are 0.067 mm/√min. The chloride content decreased greatly, 90% after a depth of 15 mm. It was noticed that the site cured samples showed higher chloride contents near surface compared to water cured samples. This investigation suggested that the developed mix design of concrete grout using locally available construction materials can be used for crack repairing of existing RC structures in Sabah.
Keywords:
Concrete grout, Salt ponding, Sorptivity, Water absorption.