A Comparative Study of Metal Extraction from Spent Catalyst Using Acidithiobacillus ferrooxidans
Abstract:
The recovery of metal values and safe disposal of spent catalyst is gaining interest due to both its hazardous nature and increased regulation associated with disposal methods. Prior to the recovery of the valuable metals, removal of entrained deposits limit the diffusion of lixiviate resulting in low recovery of metals must be taken into consideration. Therefore, petroleum refinery spent catalyst was subjected to acetone washing and roasting at 500oC. The treated samples were investigated for metals bioleaching using Acidithiobacillus ferrooxidans in batch reactors and the leaching efficiencies were compared. It was found out that acetone washed spent catalysts results in better metal recovery compare to roasted spent. About 83% Ni, 20% Al, 50% Mo and 73% V were leached using the acetone washed spent catalyst. In both the cases, Ni, V and Mo was high compared to Al.
Keywords:
Acetone wash, At. ferrooxidans, Bioleaching, Calcined, Metal recovery.
2
10084
Bioleaching of Spent Catalyst using Moderate Thermophiles with Different Pulp Densities and Varying Size Fractions without Fe Supplemented Growth Medium
Abstract:

Bioleaching of spent catalyst using moderate thermophilic chemolithotrophic acidophiles in growth medium without Fe source was investigated with two different pulp densities and three different size fractions. All the experiments were conducted on shake flasks at a temperature of 65 °C. The leaching yield of Ni and Al was found to be promising with very high leaching yield of 92-96% followed by Al as 41-76%, which means both Ni and Al leaching were favored by the moderate thermophilic bioleaching compared to the mesophilic bioleaching. The acid consumption was comparatively higher for the 10% pulp density experiments. Comparatively minimal difference in the leaching yield with different size fractions and different pulp densities show no requirement of grinding and using low pulp density less than 10%. This process would rather be economical as well as eco-friendly process for future optimization of the recovery of metal values from spent catalyst.

Keywords:
Bioleaching, spent catalyst, leaching yield, thermophile.
1
9996577
Comparison of Bioleaching of Metals from Spent Petroleum Catalyst Using Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans
Abstract:

The present investigation deals with bioleaching of spent petroleum catalyst using At. ferrooxidans and At. thiooxidans. The spent catalyst used in the present study was pretreated with acetone to remove the oily hydrocarbons. FESEM and XPS analysis indicated the presence of metals in sulfide and oxide forms in spent catalyst. Both At. ferrooxidans and At. thiooxidans were found to be highly effective in producing the acid. Bioleaching with At. ferrooxidans and At. thiooxidans led to higher recovery of metals compare to control. During bioleaching similar recoveries of metals were obtained using At. ferrooxidans and At. thiooxidans. This might be due to the presence of metals as soluble oxides and sulphides in the spent catalyst. At the end of bioleaching, about 87-90% Ni, 34% Al, 65-73% Mo and 92-97% V were leached using above bacteria. It is elucidated that bioleaching with At. thiooxidans is comparatively more advantageous due to lower cost of sulphur.  

Keywords:
Spent catalyst, At. ferrooxidans, Bioleaching, Metal recovery.